| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.11 | g/cm3 |
| 密度 | | ISO1183 | 1.11 | g/cm3 |
| 熔流率（熔体流动速率）(280°C/5.0kg) | | ASTMD1238 | 3.5 | g/10min |
| 溶化体积流率（MVR）(300°C/5.0kg) | | ISO1133 | 10.0 | cm3/10min |
| 收缩率-流动 | ——2 | InternalMethod | 0.50to0.70 | % |
| 收缩率-流动 | 3.20mm | InternalMethod | 0.50to0.70 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.18 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.060 | % |
| 拉伸模量3 | | ASTMD638 | 2500 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2500 | MPa |
| 抗张强度4(屈服) | | ASTMD638 | 70.0 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 70.0 | MPa |
| TensileStrength4(Break) | | ASTMD638 | 60.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 55.0 | MPa |
| 伸长率4(屈服) | | ASTMD638 | 5.0 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 4.0 | % |
| 伸长率4(断裂) | | ASTMD638 | 7.0 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 10 | % |
| FlexuralModulus5(50.0mmSpan) | | ASTMD790 | 2550 | MPa |
| 弯曲模量6 | | ISO178 | 2400 | MPa |
| FlexuralStress6,7 | | ISO178 | 110 | MPa |
| FlexuralStrength5(Yield,50.0mmSpan) | | ASTMD790 | 105 | MPa |
| 泰伯耐磨性(1000Cycles,1000g,CS-17转轮) | | InternalMethod | 35.0 | mg |
| 简支梁缺口冲击强度8 | -30°C | ISO179/1eA | 5.0 | kJ/m2 |
| 简支梁缺口冲击强度8 | 23°C | ISO179/1eA | 14 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 180 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 330 | J/m |
| 悬壁梁缺口冲击强度9 | -30°C | ISO180/1A | 5.0 | kJ/m2 |
| 悬壁梁缺口冲击强度9 | 23°C | ISO180/1A | 13 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 50.0 | J |
| 球压硬度(H358/30) | | ISO2039-1 | 113 | MPa |
| HeatDeflectionTemperature10(0.45MPa,Unannealed,100mmSpan) | | ISO75-2/Be | 140 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 135 | °C |
| HeatDeflectionTemperature10(1.8MPa,Unannealed,100mmSpan) | | ISO75-2/Ae | 130 | °C |
| 维卡软化温度 | | ASTMD152511 | 155 | °C |
| 维卡软化温度 | —— | ISO306/A50 | 160 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 145 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 155 | °C |
| BallPressureTest | 125°C | IEC60695-10-2 | Pass | |
| BallPressureTest | 140°C12 | IEC60695-10-2 | Pass | |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 7.5E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(23到80°C) | | ISO11359-2 | 7.0E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 7.5E-5 | cm/cm/°C |
| CLTE-Transverse(23to80°C) | | ISO11359-2 | 9.0E-5 | cm/cm/°C |
| 导热系数 | | ISO8302 | 0.27 | W/m/K |
| RTIElec | | UL746 | 110 | °C |
| RTIImp | | UL746 | 105 | °C |
| RTIStr | | UL746 | 115 | °C |
| 表面电阻率 | | IEC60093 | >1.0E+15 | ohms |
| 体积电阻率 | | IEC60093 | 1.0E+15 | ohmscm |
| 介电强度 | 0.800mm,在油中 | IEC60243-1 | 33 | kV/mm |
| 介电强度 | 1.60mm,在油中 | IEC60243-1 | 26 | kV/mm |
| 介电强度 | 3.20mm,在油中 | IEC60243-1 | 16 | kV/mm |
| 相对电容率 | 50Hz | IEC60250 | 2.80 | |
| 相对电容率 | 60Hz | IEC60250 | 2.80 | |
| 相对电容率 | 1MHz | IEC60250 | 2.70 | |
| 耗散因数 | 50Hz | IEC60250 | 9.0E-4 | |
| 耗散因数 | 60Hz | IEC60250 | 9.0E-4 | |
| 耗散因数 | 1MHz | IEC60250 | 3.0E-3 | |
| 漏电起痕指数 | | IEC60112 | 250 | V |