性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.11 | g/cm3 |
熔流率(熔体流动速率)(280°C/5.0kg) | | ASTMD1238 | 5.3 | g/10min |
收缩率-流动(3.20mm) | | InternalMethod | 0.60to0.90 | % |
拉伸模量2 | | ASTMD638 | 2140 | MPa |
抗张强度3(屈服) | | ASTMD638 | 55.2 | MPa |
抗张强度3(断裂) | | ASTMD638 | 48.3 | MPa |
伸长率3(屈服) | | ASTMD638 | 6.6 | % |
伸长率4(断裂) | | ASTMD638 | 34 | % |
弯曲模量4(50.0mm跨距) | | ASTMD790 | 2340 | MPa |
弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 89.6 | MPa |
悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 210 | J/m |
装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 44.1 | J |
载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 137 | °C |
载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 121 | °C |
维卡软化温度 | | ASTMD15255 | 152 | °C |
线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 6.3E-5 | cm/cm/°C |
线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 5.6E-5 | cm/cm/°C |