| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.11 | g/cm3 |
| 密度 | | ISO1183 | 1.11 | g/cm3 |
| 熔流率（熔体流动速率） | 280°C/5.0kg | ASTMD1238 | 18 | g/10min |
| 熔流率（熔体流动速率） | 300°C/5.0kg | ASTMD1238 | 43 | g/10min |
| 溶化体积流率（MVR） | 280°C/5.0kg | ISO1133 | 17.6 | cm3/10min |
| 溶化体积流率（MVR） | 300°C/5.0kg | ISO1133 | 41.0 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.80 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.27 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.045 | % |
| 拉伸模量2 | | ASTMD638 | 2450 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2430 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 56.2 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 54.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 46.8 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 47.8 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 4.3 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 4.0 | % |
| 伸长率4(断裂) | | ASTMD638 | 28 | % |
| 拉伸应变 | 断裂 | ISO527-2 | 28 | % |
| 拉伸应变 | 断裂 | ISO527-2/50 | 28 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 2400 | MPa |
| 弯曲模量5 | | ISO178 | 2390 | MPa |
| FlexuralStress5,6 | | ISO178 | 90.0 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 90.0 | MPa |
| 简支梁缺口冲击强度7(23°C) | | ISO179/1eA | 19 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 120 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 200 | J/m |
| 悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 11 | kJ/m2 |
| 悬壁梁缺口冲击强度8 | 23°C | ISO180/1A | 16 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 46.0 | J |
| 载荷下热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 106 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 113 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 107 | °C |
| 维卡软化温度 | | ASTMD152510 | 127 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 127 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 129 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 8.4E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-40到40°C) | | ISO11359-2 | 8.4E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 8.5E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ISO11359-2 | 8.5E-5 | cm/cm/°C |
| DraegerTubeToxicity11 | Flaming:1.52mm | | Pass | |
| DraegerTubeToxicity11 | Non-Flaming:1.52mm | | Pass | |
| FlameSpreadIndex(1.52mm) | | ASTME162 | 15.0 | |
| NBSSmokeDensity | Flaming,20min:3.20mm | ASTME662 | 126 | |
| NBSSmokeDensity | Flaming,4min:1.52mm | ASTME662 | 29.0 | |
| NBSSmokeDensity | Flaming,4min:3.20mm | ASTME662 | 35.0 | |
| NBSSmokeDensity | Non-Flaming,4min:1.52mm | ASTME662 | 7.00 | |
| VerticalBurnTest | Testa(60s,1.52mm),passesat | FAR25.853 | 0.0 | hr |
| VerticalBurnTest | Testb(12s,1.52mm),passesat | FAR25.853 | 4.00 | sec |