| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.15 | g/cm3 |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.050to0.15 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.15to0.30 | % |
| 抗张强度2(屈服) | | ASTMD638 | 79.3 | MPa |
| 抗张强度2(断裂) | | ASTMD638 | 71.0 | MPa |
| 伸长率2(断裂) | | ASTMD638 | 3.0 | % |
| FlexuralModulus3(100mmSpan) | | ASTMD790 | 6890 | MPa |
| FlexuralStrength3(Yield,100mmSpan) | | ASTMD790 | 103 | MPa |
| 泰伯耐磨性(1000Cycles,1000g,CS-17转轮) | | ASTMD1044 | 83.0 | mg |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 69 | J/m |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 240 | J/m |
| 洛氏硬度(R级) | | ASTMD785 | 122 | |
| 载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTMD648 | 111 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 105 | °C |
| RTIElec | | UL746 | 50.0 | °C |
| RTIImp | | UL746 | 50.0 | °C |
| RTIStr | | UL746 | 50.0 | °C |
| 表面电阻率 | | ASTMD257 | 1.3E+4 | ohms |
| 体积电阻率 | | ASTMD257 | 8.0E+3 | ohmscm |
| StaticDecay4 | | FTMS101B | 10 | msec |
| UL阻燃等级(2.0mm) | | UL94 | V-15VA | |