性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.20 | g/cm3 |
熔流率(熔体流动速率)(300°C/5.0kg) | | ASTMD1238 | 13 | g/10min |
收缩率-流动(3.20mm) | | InternalMethod | 0.10to0.30 | % |
MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.20to0.40 | % |
拉伸模量2 | | ASTMD638 | 6260 | MPa |
抗张强度3(屈服) | | ASTMD638 | 109 | MPa |
抗张强度3(断裂) | | ASTMD638 | 109 | MPa |
伸长率4(断裂) | | ASTMD638 | 2.4 | % |
弯曲模量4(50.0mm跨距) | | ASTMD790 | 5720 | MPa |
弯曲强度5(断裂,50.0mm跨距) | | ASTMD790 | 170 | MPa |
悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 100 | J/m |
悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 510 | J/m |
装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 16.5 | J |
载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 164 | °C |
载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 159 | °C |
维卡软化温度 | | ASTMD15255 | 175 | °C |
DielectricStrength(1.60mm,inOil) | | ASTMD149 | 34 | kV/mm |