| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.28 | g/cm3 |
| 熔流率（熔体流动速率）(280°C/5.0kg) | | ASTMD1238 | 20 | g/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.10to0.20 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.20to0.40 | % |
| 拉伸模量2 | | ASTMD638 | 7760 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 108 | MPa |
| 伸长率4(断裂) | | ASTMD638 | 1.5 | % |
| 弯曲模量 | 100mmSpan4 | ASTMD790 | 7170 | MPa |
| 弯曲模量 | 50.0mm跨距5 | ASTMD790 | 8340 | MPa |
| 弯曲强度 | 断裂,50.0mm跨距5 | ASTMD790 | 162 | MPa |
| 弯曲强度 | Break,100mmSpan4 | ASTMD790 | 131 | MPa |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 91 | J/m |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 260 | J/m |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 14.0 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 129 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 122 | °C |
| 维卡软化温度 | | ASTMD15256 | 131 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 2.0E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 6.7E-5 | cm/cm/°C |