| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.19 | g/cm3 |
| 密度 | | ISO1183 | 1.19 | g/cm3 |
| 熔流率（熔体流动速率）(280°C/5.0kg) | | ASTMD1238 | 6.0 | g/10min |
| 溶化体积流率（MVR）(280°C/5.0kg) | | ISO1133 | 6.00 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.20to0.25 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.40to0.60 | % |
| 拉伸模量2 | | ASTMD638 | 7600 | MPa |
| 拉伸模量 | | ISO527-2/1 | 7700 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 101 | MPa |
| 拉伸应力(屈服) | | ISO527-2/5 | 98.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 101 | MPa |
| 拉伸应力(断裂) | | ISO527-2/5 | 98.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 2.9 | % |
| 拉伸应变(屈服) | | ISO527-2/5 | 3.2 | % |
| 伸长率4(断裂) | | ASTMD638 | 100 | % |
| 拉伸应变(断裂) | | ISO527-2/5 | 3.2 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 6600 | MPa |
| 弯曲模量5 | | ISO178 | 7100 | MPa |
| FlexuralStress5,6 | | ISO178 | 141 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 144 | MPa |
| 简支梁无缺口冲击强度7 | -30°C | ISO179/1eU | 36 | kJ/m2 |
| 简支梁无缺口冲击强度7 | 23°C | ISO179/1eU | 39 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 95 | J/m |
| NotchedIzodImpactStrength8(23°C) | | ISO180/1A | 10 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 650 | J/m |
| 无缺口伊佐德冲击强度8 | -30°C | ISO180/1U | 42 | kJ/m2 |
| 无缺口伊佐德冲击强度8 | 23°C | ISO180/1U | 42 | kJ/m2 |
| 装有测量仪表的落镖冲击 | -30°C,TotalEnergy | ASTMD3763 | 10.0 | J |
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 15.0 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 166 | °C |
| HeatDeflectionTemperature9(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 168 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 156 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 153 | °C |
| 维卡软化温度 | | ISO306/B120 | 150 | °C |
| BallPressureTest(125°C) | | IEC60695-10-2 | Pass | |
| 线形热膨胀系数-流动(-40到95°C) | | ASTME831 | 2.5E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-30到80°C) | | ISO11359-2 | 2.5E-5 | cm/cm/°C |
| CLTE-Transverse(-40to95°C) | | ASTME831 | 1.3E-4 | cm/cm/°C |
| CLTE-Transverse(-30to80°C) | | ISO11359-2 | 1.2E-4 | cm/cm/°C |
| FlameRating(1.0mm) | | UL94 | HB | |
| 灼热丝易燃指数(3.0mm) | | IEC60695-2-12 | 650 | °C |