| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.31 | g/cm3 |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.10to0.40 | % |
| 吸水率(24hr) | | ASTMD570 | 0.060 | % |
| 抗张强度2(断裂) | | ASTMD638 | 121 | MPa |
| 伸长率2(断裂) | | ASTMD638 | 5.0 | % |
| FlexuralModulus3(100mmSpan) | | ASTMD790 | 7790 | MPa |
| FlexuralStrength3(Yield,100mmSpan) | | ASTMD790 | 172 | MPa |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 96 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 120 | J/m |
| 洛氏硬度(L计秤) | | ASTMD785 | 108 | |
| 载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTMD648 | 141 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 135 | °C |
| 线形热膨胀系数-流动(-40到95°C) | | ASTME831 | 2.5E-5 | cm/cm/°C |
| RTIElec | | UL746 | 110 | °C |
| RTIImp | | UL746 | 105 | °C |
| RTIStr | | UL746 | 110 | °C |
| DielectricStrength(3.20mm,inOil) | | ASTMD149 | 21 | kV/mm |
| 介电常数 | 50Hz | ASTMD150 | 3.15 | |
| 介电常数 | 60Hz | ASTMD150 | 3.15 | |
| 耗散因数 | 50Hz | ASTMD150 | 2.0E-3 | |
| 耗散因数 | 60Hz | ASTMD150 | 2.0E-3 | |
| 耐电弧性4 | | ASTMD495 | PLC6 | |
| 相比耐漏电起痕指数(CTI) | | UL746 | PLC3 | |
| 高电弧燃烧指数(HAI) | | UL746 | PLC2 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC4 | |
| 热丝引燃(HWI) | | UL746 | PLC0 | |
| UL阻燃等级 | 1.5mm | UL94 | V-1 | |
| UL阻燃等级 | 6.0mm | UL94 | V-0 | |
| 极限氧指数 | | ASTMD2863 | 36 | % |