性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.04 | g/cm3 |
溶化体积流率(MVR)(220°C/10.0kg) | | ISO1133 | 9.00 | cm3/10min |
收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
拉伸模量2 | | ASTMD638 | 2140 | MPa |
抗张强度3(屈服) | | ASTMD638 | 40.0 | MPa |
抗张强度3(断裂) | | ASTMD638 | 33.1 | MPa |
伸长率3(屈服) | | ASTMD638 | 2.4 | % |
伸长率4(断裂) | | ASTMD638 | 43 | % |
弯曲模量4(50.0mm跨距) | | ASTMD790 | 2410 | MPa |
弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 73.4 | MPa |
悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 420 | J/m |
装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 35.0 | J |
载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 94.4 | °C |
载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 82.2 | °C |
维卡软化温度 | | ASTMD15255 | 107 | °C |
线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 7.9E-5 | cm/cm/°C |
线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 8.1E-5 | cm/cm/°C |
充模分析 | | TestMethod | NominalValue | Unit |
MeltViscosity(240°C,100sec^-1) | | ASTMD3835 | 1160 | Pas |