| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.08 | g/cm3 |
| 密度 | | ISO1183 | 1.08 | g/cm3 |
| 熔流率（熔体流动速率）(280°C/5.0kg) | | ASTMD1238 | 7.0 | g/10min |
| 溶化体积流率（MVR）(280°C/5.0kg) | | ISO1133 | 7.00 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.23 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.060 | % |
| 拉伸模量2 | | ASTMD638 | 2300 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2350 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 64.0 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 63.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 53.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 52.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 4.8 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 4.6 | % |
| 伸长率4(断裂) | | ASTMD638 | 30 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 30 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 2400 | MPa |
| 弯曲模量5 | | ISO178 | 2300 | MPa |
| FlexuralStress5,6 | | ISO178 | 92.0 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 97.0 | MPa |
| 泰伯耐磨性(1000Cycles,1000g,CS-17转轮) | | InternalMethod | 60.0 | mg |
| 简支梁缺口冲击强度7 | -30°C | ISO179/1eA | 7.0 | kJ/m2 |
| 简支梁缺口冲击强度7 | 23°C | ISO179/1eA | 14 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 70 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 120 | J/m |
| 悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 7.0 | kJ/m2 |
| 悬壁梁缺口冲击强度8 | 23°C | ISO180/1A | 11 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 41.0 | J |
| 洛氏硬度(R级) | | ISO2039-2 | 119 | |
| 球压硬度(H358/30) | | ISO2039-1 | 105 | MPa |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 133 | °C |
| HeatDeflectionTemperature9(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 133 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 119 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 118 | °C |
| 维卡软化温度 | | ASTMD152510 | 139 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 138 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 142 | °C |
| BallPressureTest(125°C) | | IEC60695-10-2 | Pass | |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 8.2E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-40到40°C) | | ISO11359-2 | 8.2E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 8.5E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ISO11359-2 | 8.5E-5 | cm/cm/°C |
| 表面电阻率 | | IEC60093 | >1.0E+15 | ohms |
| 体积电阻率 | | IEC60093 | 1.0E+15 | ohmscm |
| 介电强度(3.20mm,在油中) | | IEC60243-1 | 16 | kV/mm |
| 相对电容率 | 50Hz | IEC60250 | 2.70 | |
| 相对电容率 | 60Hz | IEC60250 | 2.70 | |
| 相对电容率 | 1MHz | IEC60250 | 2.70 | |
| 耗散因数 | 50Hz | IEC60250 | 4.0E-4 | |
| 耗散因数 | 60Hz | IEC60250 | 4.0E-4 | |
| 耗散因数 | 1MHz | IEC60250 | 2.0E-3 | |
| UL阻燃等级(1.5mm) | | UL94 | V-1 | |
| 灼热丝易燃指数(3.2mm) | | IEC60695-2-12 | 960 | °C |
| 热灯丝点火温度(3.0mm) | | IEC60695-2-13 | 700 | °C |
| 极限氧指数 | | ISO4589-2 | 30 | % |
| Gardner光泽度(60°,无织构) | | ASTMD523 | 20 | |