| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.19 | g/cm3 |
| 熔流率（熔体流动速率）(260°C/5.0kg) | | ASTMD1238 | 2.6 | g/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.20to0.23 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.25to0.76 | % |
| 抗张强度2(屈服) | | ASTMD638 | 79.3 | MPa |
| 抗张强度2(断裂) | | ASTMD638 | 79.3 | MPa |
| 伸长率2(断裂) | | ASTMD638 | 7.7 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 5560 | MPa |
| FlexuralStrength3(Break,50.0mmSpan) | | ASTMD790 | 130 | MPa |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 100 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 170 | J/m |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 830 | J/m |
| 装有测量仪表的落镖冲击 | -30°C,TotalEnergy | ASTMD3763 | 20.4 | J |
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 19.1 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 155 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 134 | °C |
| 维卡软化温度 | | ASTMD15254 | 162 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 1.4E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 7.7E-5 | cm/cm/°C |
| UL阻燃等级(1.5mm) | | UL94 | HB | |