| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.11 | g/cm3 |
| 熔流率（熔体流动速率）(260°C/5.0kg) | | ASTMD1238 | 5.5 | g/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.55to0.70 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.45to0.70 | % |
| 拉伸模量2 | | ASTMD638 | 2170 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 39.3 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 37.9 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 2.8 | % |
| 伸长率4(断裂) | | ASTMD638 | 55 | % |
| 弯曲模量 | 50.0mm跨距4 | ASTMD790 | 2070 | MPa |
| 弯曲模量 | 100mmSpan5 | ASTMD790 | 2000 | MPa |
| 弯曲强度 | 屈服,50.0mm跨距4 | ASTMD790 | 61.4 | MPa |
| 弯曲强度 | Yield,100mmSpan5 | ASTMD790 | 57.2 | MPa |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 230 | J/m |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 2200 | J/m |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 32.2 | J |
| 载荷下热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 113 | °C |
| 载荷下热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 117 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 97.2 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 106 | °C |
| 维卡软化温度 | | ASTMD15256 | 110 | °C |
| 线形热膨胀系数-流动(-40到60°C) | | ASTME831 | 6.5E-5 | cm/cm/°C |
| CLTE-Transverse(-40to60°C) | | ASTME831 | 7.4E-5 | cm/cm/°C |