| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.40 | g/cm3 |
| 密度 | | ASTMD792 | 1.45 | g/cm3 |
| 收缩率-流量(24小时) | | ASTMD955 | 2.0to4.0 | % |
| MoldingShrinkage-AcrossFlow(24hr) | | ASTMD955 | 2.0to4.0 | % |
| 吸水率(24hr,50%RH) | | ASTMD570 | 0.21 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.35 | % |
| 拉伸模量2 | | ASTMD638 | 2870 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2590 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 41.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/5 | 39.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 8.5 | % |
| 拉伸应变(屈服) | | ISO527-2/5 | 8.8 | % |
| 伸长率4(断裂) | | ASTMD638 | 14 | % |
| 拉伸应变(断裂) | | ISO527-2/5 | 14 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 2430 | MPa |
| 弯曲模量5 | | ISO178 | 2420 | MPa |
| 弯曲应力 | | ISO178 | 62.0 | MPa |
| 摩擦系数 | Dynamic | ASTMD3702Modified | 0.23 | |
| 摩擦系数 | Static | ASTMD3702Modified | 0.16 | |
| 磨损因数-Washer | | ASTMD3702Modified | 8.00 | 10^-10in^5-min/ft-lb-hr |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 36 | J/m |
| 悬壁梁缺口冲击强度6(23°C) | | ISO180/1A | 5.0 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 370 | J/m |
| 无缺口伊佐德冲击强度5(23°C) | | ISO180/1U | 26 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 5.00 | J |
| 多轴向仪器化冲击能量 | | ISO6603-2 | 1.00 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 155 | °C |
| HeatDeflectionTemperature7(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 147 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 94.0 | °C |
| 热变形温度7(1.8MPa,未退火,64.0mm跨距) | | ISO75-2/Af | 84.0 | °C |
| 线形热膨胀系数-流动(-30到30°C) | | ASTMD696 | 9.9E-5 | cm/cm/°C |
| CLTE-Transverse(-30to30°C) | | ASTMD696 | 1.0E-4 | cm/cm/°C |