| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.20 | g/cm3 |
| 特定体积 | | ASTMD792 | 0.835 | cm3/g |
| 密度 | | ASTMD792 | 1.19 | g/cm3 |
| 熔流率（熔体流动速率）(300°C/1.2kg) | | ASTMD1238 | 18 | g/10min |
| 溶化体积流率（MVR）(300°C/1.2kg) | | ISO1133 | 16.0 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| 吸水率(24hr) | | ASTMD570 | 0.15 | % |
| 吸水率 | 平衡,23°C | ASTMD570 | 0.35 | % |
| 吸水率 | 平衡,100°C | ASTMD570 | 0.58 | % |
| 拉伸模量2 | | ASTMD638 | 2380 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2350 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 62.1 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 63.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 68.9 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 65.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 7.0 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 6.0 | % |
| 伸长率4(断裂) | | ASTMD638 | 130 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 100 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 2140 | MPa |
| 弯曲模量5 | | ISO178 | 2300 | MPa |
| FlexuralStress5,6 | | ISO178 | 90.0 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 96.5 | MPa |
| 泰伯耐磨性(1000Cycles,1000g,CS-17转轮) | | ASTMD1044 | 10.0 | mg |
| 简支梁缺口冲击强度 | 23°C7 | ISO179/1eA | 10 | kJ/m2 |
| 简支梁缺口冲击强度 | 23°C | ISO179/2C | 35 | kJ/m2 |
| 简支梁无缺口冲击强度7 | -30°C | ISO179/1eU | NoBreak | |
| 简支梁无缺口冲击强度7 | 23°C | ISO179/1eU | NoBreak | |
| 悬壁梁缺口冲击强度 | Colors | ASTMD256 | 110to690 | J/m |
| 悬壁梁缺口冲击强度 | Natural,Tints | ASTMD256 | 690 | J/m |
| NotchedIzodImpactStrength8(23°C) | | ISO180/1A | 12 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 3200 | J/m |
| 无缺口伊佐德冲击强度8 | -30°C | ISO180/1U | NoBreak | |
| 无缺口伊佐德冲击强度8 | 23°C | ISO180/1U | NoBreak | |
| 装有测量仪表的落镖冲击(23°C,EnergyatPeakLoad) | | ASTMD3763 | 62.1 | J |
| 落锤冲击(23°C) | | ASTMD3029 | 169 | J |
| 拉伸冲击强度9 | | ASTMD1822 | 473 | kJ/m2 |
| 洛氏硬度 | M计秤 | ASTMD785 | 70 | |
| 洛氏硬度 | R计秤 | ASTMD785 | 118 | |
| 载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTMD648 | 138 | °C |
| HeatDeflectionTemperature10(0.45MPa,Unannealed,100mmSpan) | | ISO75-2/Be | 133 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 129 | °C |
| HeatDeflectionTemperature10(1.8MPa,Unannealed,100mmSpan) | | ISO75-2/Ae | 122 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 140 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 141 | °C |
| BallPressureTest(125°C) | | IEC60695-10-2 | Pass | |
| 线形热膨胀系数-流动(-40到95°C) | | ASTME831 | 6.8E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(23到80°C) | | ISO11359-2 | 7.0E-5 | cm/cm/°C |
| 比热 | | ASTMC351 | 1260 | J/kg/°C |
| 导热系数 | | ASTMC177 | 0.19 | W/m/K |
| 导热系数 | | ISO8302 | 0.20 | W/m/K |
| 表面电阻率 | | IEC60093 | >1.0E+15 | ohms |
| 体积电阻率 | | ASTMD257 | >1.0E+17 | ohmscm |
| 体积电阻率 | | IEC60093 | >1.0E+15 | ohmscm |
| 介电强度(3.20mm,inAir) | | ASTMD149 | 15 | kV/mm |
| 介电强度(3.20mm,在油中) | | IEC60243-1 | 17 | kV/mm |
| 介电常数 | 50Hz | ASTMD150 | 3.17 | |
| 介电常数 | 60Hz | ASTMD150 | 3.17 | |
| 介电常数 | 1MHz | ASTMD150 | 2.96 | |
| 相对电容率 | 50Hz | IEC60250 | 2.70 | |