| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.30 | g/cm3 |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.80to1.0 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.80to1.0 | % |
| 室外适用性 | | UL746C | f2 | |
| 抗张强度2(屈服) | | ASTMD638 | 46.9 | MPa |
| 抗张强度2(断裂) | | ASTMD638 | 40.0 | MPa |
| 伸长率2(屈服) | | ASTMD638 | 5.0 | % |
| 伸长率2(断裂) | | ASTMD638 | 70 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 1860 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 66.9 | MPa |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 430 | J/m |
| 悬壁梁缺口冲击强度 | -20°C | ASTMD256 | 690 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 750 | J/m |
| 装有测量仪表的落镖冲击 | -40°C,TotalEnergy | ASTMD3763 | 47.5 | J |
| 装有测量仪表的落镖冲击 | -20°C,TotalEnergy | ASTMD3763 | 44.7 | J |
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 45.2 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 103 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 68.3 | °C |
| 维卡软化温度 | | ASTMD15254 | 115 | °C |
| 维卡软化温度 | | ISO306/B120 | 122 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 9.5E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-40到40°C) | | ISO11359-2 | 9.5E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 9.8E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ISO11359-2 | 1.0E-4 | cm/cm/°C |
| RTIElec | | UL746 | 75.0 | °C |
| RTIImp | | UL746 | 75.0 | °C |
| RTIStr | | UL746 | 75.0 | °C |
| 耐电弧性5 | | ASTMD495 | PLC5 | |
| 相比耐漏电起痕指数(CTI) | | UL746 | PLC0 | |
| 高电弧燃烧指数(HAI) | | UL746 | PLC0 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC2 | |
| 热丝引燃(HWI) | | UL746 | PLC2 | |
| UL阻燃等级 | 1.5mm | UL94 | V-0 | |
| UL阻燃等级 | 3.0mm | UL94 | 5VA | |
| 极限氧指数 | | ASTMD2863 | 28 | % |