| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.28 | g/cm3 |
| 密度 | | ASTMD792 | 1.28 | g/cm3 |
| 收缩率-流量(24小时) | | ASTMD955 | 0.80to1.0 | % |
| MoldingShrinkage-AcrossFlow(24hr) | | ASTMD955 | 0.40to0.60 | % |
| 吸水率(24hr,50%RH) | | ASTMD570 | 0.67 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.89 | % |
| 拉伸模量2 | | ASTMD638 | 65.0 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 19.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 18.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 390 | % |
| 伸长率4(断裂) | | ASTMD638 | 390 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 63.0 | MPa |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 39.8 | J |
| 多轴向仪器化冲击能量 | | ISO6603-2 | 41.0 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 23.0 | °C |
| HeatDeflectionTemperature5(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 23.0 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 23.0 | °C |
| 热变形温度5(1.8MPa,未退火,64.0mm跨距) | | ISO75-2/Af | 23.0 | °C |
| 表面电阻率 | | ASTMD257 | 1.0E+2to1.0E+5 | ohms |