| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.01 | g/cm3 |
| 密度 | | ISO1183 | 1.01 | g/cm3 |
| 熔流率（熔体流动速率）(200°C/5.0kg) | | ASTMD1238 | 13 | g/10min |
| 溶化体积流率（MVR）(200°C/5.0kg) | | ISO1133 | 14.0 | cm3/10min |
| 收缩率-流动 | | ASTMD955 | 0.65 | % |
| 收缩率 | | ISO294-4 | 0.30to1.0 | % |
| 吸水率(饱和,23°C) | | ASTMD570 | 0.070 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.070 | % |
| 拉伸模量 | | ASTMD638 | 1170 | MPa |
| 拉伸模量 | | ISO527-2 | 900 | MPa |
| 抗张强度(屈服,23°C) | | ASTMD638 | 16.0 | MPa |
| 拉伸应力(屈服,23°C) | | ISO527-2 | 15.0 | MPa |
| 拉伸应变(屈服,23°C) | | ISO527-2 | 2.0 | % |
| 伸长率(断裂,23°C) | | ASTMD638 | >300 | % |
| 标称拉伸断裂应变(23°C) | | ISO527-2 | >300 | % |
| 弯曲模量 | | ASTMD790 | 758 | MPa |
| 弯曲模量 | | ISO178 | 900 | MPa |
| 弯曲强度 | | ASTMD790 | 17.0 | MPa |
| 弯曲应力 | 5.0%应变 | | 18.0 | MPa |
| 弯曲应力 | —— | ISO178 | 18.0 | MPa |
| 弹性模量-MD | | ASTMD882 | 834 | MPa |
| 弹性模量-TD | | ASTMD882 | 685 | MPa |
| 伸长率-MD(断裂) | | ASTMD882 | 310 | % |
| TensileElongation-TD(Break) | | ASTMD882 | 350 | % |
| 伸长率-MD(断裂) | | ISO527-3 | >300 | % |
| 埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 830 | g |
| ElmendorfTearStrength-TD | | ASTMD1922 | 340 | g |
| OxygenTransmissionRate(23°C,0%RH) | | ASTMD3985 | 120000 | cm3/m2/24hr |
| WaterVaporTransmissionRate2(23°C) | | ASTMF1249 | 410 | g/m2/24hr |
| 简支梁缺口冲击强度(23°C) | | ISO179 | 85 | kJ/m2 |
| 简支梁无缺口冲击强度(23°C) | | ISO179 | NoBreak | |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | NoBreak | |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/A | 4.0 | kJ/m2 |
| 悬壁梁缺口冲击强度 | 23°C | ISO180/A | 5.0 | kJ/m2 |
| 装有测量仪表的落镖冲击 | Peakforce | ASTMD3763 | 10.0 | J |
| 装有测量仪表的落镖冲击 | Totalenergy | ASTMD3763 | 21.1 | J |
| 肖氏硬度 | 邵氏A | ISO868 | 97 | |
| 肖氏硬度 | 邵氏D | ISO868 | 58 | |
| 载荷下热变形温度(0.45MPa,未退火) | | ASTMD648 | 66.7 | °C |
| HeatDeflectionTemperature3(0.45MPa,Annealed) | | ISO75-2/B | 62.0 | °C |
| 载荷下热变形温度(1.8MPa,未退火) | | ASTMD648 | 45.6 | °C |
| HeatDeflectionTemperature3(1.8MPa,Annealed) | | ISO75-2/A | 51.0 | °C |
| 维卡软化温度 | | ASTMD15254 | 71.7 | °C |
| 维卡软化温度 | —— | ISO306/A50 | 67.0 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 35.0 | °C |
| 线形热膨胀系数-流动 | | ASTMD696 | 1.3E-4 | cm/cm/°C |
| 线形热膨胀系数-流动 | | ISO11359-2 | 6.0E-5to9.0E-5 | cm/cm/°C |
| 表面电阻率 | | IEC60093 | >1.0E+15 | ohms |
| 体积电阻率 | | IEC60093 | >1.0E+15 | ohmscm |
| 介电常数(100Hz) | | IEC60250 | 2.50 | |
| 耗散因数 | 100Hz | IEC60250 | 3.0E-4 | |
| 耗散因数 | 1MHz | IEC60250 | 8.0E-4 | |
| 漏电起痕指数 | | IEC60112 | 600 | V |
| 折射率5 | | ASTMD542 | 1.570 | |
| 折射率 | | ISO489 | 1.570 | |
| 透射率(550nm) | | ASTMD1003 | 90.0 | % |
| 雾度 | | ASTMD1003 | 1.6 | % |