| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度 | | ISO1183 | 0.840to0.940 | g/cm3 |
| 弹性体 | | TestMethod | NominalValue | Unit |
| TensileSet2(70°C,1320min) | | InternalMethod | 45 | % |
| TensileStress-Flow3(100%Strain) | | ISO37 | 2.80 | MPa |
| TensileStress-Flow3(Yield) | | ISO37 | 6.20 | MPa |
| TensileElongation-Flow3(Break) | | ISO37 | 550 | % |
| 撕裂强度4 | 横向流量 | ISO34-1 | 33 | kN/m |
| 撕裂强度4 | 流量 | ISO34-1 | 17 | kN/m |
| 压缩永久变形 | 23°C,72hr | ISO815 | 20 | % |
| 压缩永久变形 | 70°C,24hr | ISO815 | 33 | % |
| 肖氏硬度(邵氏A,15秒) | | ISO868 | 47 | |
| 脆化温度 | | ASTMD746 | -60.0 | °C |
| ChangeinTensileStrengthinAir5(100°C,1000hr) | | ISO188 | 17 | % |
| ChangeinTensileStrainatBreakinAir5(100°C,1000hr) | | ISO188 | 4.0 | % |
| ChangeinShoreHardnessinAir5(ShoreA,100°C,1000hr) | | ISO188 | 1.0 | |
| ContinuousUpperTemperatureResistance6(3hr) | | | 150 | °C |
| ChangeinLengthinAir5 | | ISO188 | -1.0 | % |
| ChangeinVolumeinAir5 | | ISO188 | -1.9 | % |
| 燃烧速率 | | | 42 | mm/min |
| Fogging-Reflectance7 | | SAEJ1756 | 61 | % |
| 补充信息 | | TestMethod | NominalValue | Unit |
| OdorRating-Dry8 | | MultipleStandards | 2.00 | |
| OzoneResistance9 | | | 0.00 | |