性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.01 | g/cm3 |
熔流率(熔体流动速率)(200°C/5.0kg) | | ASTMD1238 | 7.5 | g/10min |
薄膜厚度-经测试 | | | 25 | um |
SecantModulus-1%Secant,MD(25um,BlownFilm) | | ASTMD882 | 1410 | MPa |
SecantModulus-1%Secant,TD(25um,BlownFilm) | | ASTMD882 | 965 | MPa |
TensileStrength-MD(Yield,25um,BlownFilm) | | ASTMD882 | 34.5 | MPa |
TensileStrength-TD(Yield,25um,BlownFilm) | | ASTMD882 | 21.0 | MPa |
TensileElongation-MD(Break,25um,BlownFilm) | | ASTMD882 | 110 | % |
TensileElongation-TD(Break,25um,BlownFilm) | | ASTMD882 | 200 | % |
落锤冲击2(25um,吹塑薄膜) | | ASTMD1709 | 590 | g |
ElmendorfTearStrength-MD(25um,BlownFilm) | | ASTMD1922 | 7.0 | g |
ElmendorfTearStrength-TD(25um,BlownFilm) | | ASTMD1922 | 15 | g |
OxygenPermeability(25um,BlownFilm) | | ASTMD3985 | 170 | cm3mm/m2/atm/24hr |
水气透过率(25um,吹塑薄膜) | | ASTMF1249 | 2.2 | gmm/m2/atm/24hr |
装有测量仪表的落镖冲击(0.0254mm,吹塑薄膜) | | ASTMD3763 | 0.904 | J |
维卡软化温度3 | | ASTMD1525 | 85.0 | °C |
GardnerGloss(25.4um,BlownFilm) | | ASTMD523 | 140 | |
Haze4(BlownFilm) | | ASTMD1003 | 0.70 | % |