性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ISO 1183 | 0.9 | G/cm3 |
熔体流动速率 | 230°C/2.16 kg | ASTM D1238 | 2 | g/10min |
拉伸模量 | 1% Secant, MD: 50.0 um, Blown Film | ISO 527-3 | 810 | Mpa |
拉伸模量 | 1% Secant, TD: 50.0 um, Blown Film | ISO 527-3 | 790 | Mpa |
拉伸强度 | TD: Break, 50.0 um, Blown Film | ISO 527-3 | 32 | Mpa |
拉伸强度 | MD: Break, 50.0 um, Blown Film | ISO 527-3 | 47 | Mpa |
拉伸应变 | TD: Break, 50.0 um, Blown Film | ISO 527-3 | 500 | % |
拉伸应变 | MD: Break, 50.0 um, Blown Film | ISO 527-3 | 580 | % |
热变形温度 | 0.45Mpa, Unannealed | ISO 75-2/B | 80 | ℃ |
维卡软化温度 | | ISO 306/A | 129 | ℃ |
光泽度 | 45°, 50.0 um, Blown Film | ASTM D2457 | 80 | |
雾度 | 50.0 um, Blown Film | ASTM D1003 | 3 | % |