| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度 | | ASTMD1505 | 0.931 | g/cm3 |
| 熔流率（熔体流动速率）(190°C/2.16kg) | | ASTMD1238 | 2.0 | g/10min |
| 醋酸乙烯含量 | | | 8.5 | wt% |
| 抗张强度(断裂,模压成型) | | ASTMD638 | 19.0 | MPa |
| 伸长率(断裂,模压成型) | | ASTMD638 | 700 | % |
| SecantModulus-2%Secant,MD(50um,BlownFilm) | | ASTMD882 | 76.0 | MPa |
| SecantModulus-2%Secant,TD(50um,BlownFilm) | | ASTMD882 | 79.0 | MPa |
| TensileStrength-MD(Break,50um,BlownFilm) | | ASTMD882 | 31.0 | MPa |
| TensileStrength-TD(Break,50um,BlownFilm) | | ASTMD882 | 24.0 | MPa |
| TensileElongation-MD(Break,50um,BlownFilm) | | ASTMD882 | 650 | % |
| TensileElongation-TD(Break,50um,BlownFilm) | | ASTMD882 | 1100 | % |
| 落锤冲击(50um,吹塑薄膜) | | ASTMD1709B | 180 | g |
| ElmendorfTearStrength-MD(50um,BlownFilm) | | ASTMD1922 | 200 | g |
| ElmendorfTearStrength-TD(50um,BlownFilm) | | ASTMD1922 | 220 | g |
| 肖氏硬度 | 邵氏A,模压成型 | ASTMD2240 | 93 | |
| 肖氏硬度 | 邵氏D,模压成型 | ASTMD2240 | 45 | |
| 维卡软化温度 | | ASTMD15252 | 79.0 | °C |
| 熔融峰值温度 | | ASTMD3418 | 100 | °C |
| 光泽度(45°,50.0um,吹塑薄膜) | | ASTMD2457 | 90 | |
| 雾度(50.0um,吹塑薄膜) | | ASTMD1003 | 3.0 | % |