| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度 | | ASTMD792 | 0.920 | g/cm3 |
| 湿度 | | 内部方法 | <200 | ppm |
| 拉伸应力(断裂) | | ASTMD638 | 20.0 | MPa |
| 拉伸应变(断裂) | | ASTMD638 | 500 | % |
| ChangeinTensileProperties-7days(135°C) | | ASTMD638 | <25 | % |
| 热固性 | ElongationunderLoad:200°C | IEC60811-2-1 | <100 | % |
| 热固性 | ElongationwithoutLoad:200°C | IEC60811-2-1 | <10 | % |
| 体积电阻率(23°C) | | ASTMD257 | >1.0E+16 | ohmscm |
| 介电强度 | 3.18mm2 | ASTMD149 | >30 | kV/mm |
| 介电强度 | 3.18mm3 | ASTMD149 | >23 | kV/mm |
| 介电强度 | 3.18mm4 | ASTMD149 | >39 | kV/mm |
| 介电常数(23°C) | | ASTMD150 | 2.30 | |
| 耗散因数(23°C) | | ASTMD150 | <3.0E-3 | |