| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度 | | ISO1183/A | 1.41 | g/cm3 |
| 溶化体积流率（MVR）(190°C/2.16kg) | | ISO1133 | 21.0 | cm3/10min |
| 球压硬度(H358/30) | | ISO2039-1 | 137 | MPa |
| 拉伸模量 | | ISO527-2/1A/1 | 2800 | MPa |
| 拉伸应力(屈服) | | ISO527-2/1A/50 | 62.0 | MPa |
| 拉伸应变(屈服) | | ISO527-2/1A/50 | 9.0 | % |
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 7.0 | kJ/m2 |
| 简支梁缺口冲击强度 | 23°C | ISO179/1eA | 8.0 | kJ/m2 |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 无断裂 | |
| 简支梁无缺口冲击强度 | 23°C | ISO179/1eU | 无断裂 | |
| 热变形温度(1.8MPa,未退火) | | ISO75-2/Af | 94.0 | °C |
| 维卡软化温度 | | ISO306/B50 | 147 | °C |
| 表面电阻率 | | IEC60093 | >1.0E+15 | ohms |
| 体积电阻率 | | IEC60093 | >1.0E+13 | ohmscm |
| EmissionofOrganicCompounds | VDA277,TVOC(totalorganiccompounds) | VDA277 | <5.00 | ugC/g |
| EmissionofOrganicCompounds | VDA278,Fog(condensablecompounds) | VDA278 | <5.00 | ugC/g |
| EmissionofOrganicCompounds | VDA278,VOC(volatileorganiccompounds) | VDA278 | <0.950 | ugC/g |
| FormaldehydeEmissions | | VDA275 | <2.00 | mg/kg |
| Odor | | VDA270 | 3.00 | |