性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.933 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 1.1 | g/10min |
醋酸乙烯含量 | | | 9.0 | wt% |
弯曲模量-1%正割 | | ASTMD790 | 123 | MPa |
TensileStrength-MD2(Break) | | ASTMD882A | 23.0 | MPa |
TensileStrength-TD2(Break) | | ASTMD882A | 24.0 | MPa |
TensileElongation-MD2(Break) | | ASTMD882A | 380 | % |
TensileElongation-TD2(Break) | | ASTMD882A | 550 | % |
维卡软化温度 | | ASTMD1525 | 82.0 | °C |
熔融峰值温度 | | ASTMD3418 | 102 | °C |