| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | —— | ISO1183 | 2.13 | g/cm3 |
| 比重 | —— | ASTMD792 | 2.13 | g/cm3 |
| 熔流率（熔体流动速率）(372°C/5.0kg) | | ASTMD2116 | 22 | g/10min |
| 熔流率（熔体流动速率）(372°C/5.0kg) | | ISO12086 | 22 | g/10min |
| 吸水率(24hr) | | ASTMD570 | <0.010 | % |
| 抗张强度(屈服,23°C) | | ASTMD638 | 22.0 | MPa |
| 拉伸应力(屈服,23°C) | | ISO12086 | 22.0 | MPa |
| 伸长率(断裂,23°C) | | ASTMD638 | 300 | % |
| 拉伸应变(断裂,23°C) | | ISO12086 | 300 | % |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | NoBreak | |
| 悬壁梁缺口冲击强度(23°C) | | ISO180 | NoBreak | |
| 肖氏硬度(邵氏D) | | ASTMD2240 | 56 | |
| 肖氏硬度(邵氏D) | | ISO868 | 56 | |
| 连续使用温度2 | | | 205 | °C |
| 熔融温度5 | | | 255 | °C |
| DielectricStrength4(0.250mm) | | ASTMD149 | >85 | kV/mm |
| ElectricStrength(0.250mm) | | IEC60243-1 | >85 | kV/mm |
| 介电常数 | 1kHz | ASTMD150 | 2.03 | |
| 介电常数 | 1.00GHz | ASTMD150 | 2.03 | |
| 相对电容率 | 1kHz | IEC60250 | 2.03 | |
| 相对电容率 | 1.00GHz | IEC60250 | 2.03 | |
| 耗散因数 | 1kHz | ASTMD150 | 7.0E-5 | |
| 耗散因数 | 1.00GHz | ASTMD150 | 1.2E-3 | |
| 耗散因数 | 1kHz | IEC60250 | 7.0E-5 | |
| 耗散因数 | 1.00GHz | IEC60250 | 1.2E-3 | |
| UL阻燃等级5 | | UL94 | V-0 | |
| 极限氧指数 | | ASTMD2863 | >95 | % |
| 极限氧指数 | | ISO4589-2 | >95 | % |
| 补充信息 | | TestMethod | NominalValue | Unit |
| CriticalShearRate(372°C) | | InternalMethod | 155 | sec^-1 |
| GuideDDRRange-forcableextrusion | | | 60.0to100 | |
| MITFoldingEndurance-film(200.0um) | | ASTMD2176 | 5.0E+3 | Cycles |