性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.940 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 2.4 | g/10min |
甲基丙烯酸含量 | | | 21.5 | wt% |
抗张强度2(断裂) | | ASTMD638 | 10.0 | MPa |
伸长率2(断裂) | | ASTMD638 | 810 | % |
SecantModulus-1%Secant,MD | | ASTMD882 | 39.0 | MPa |
SecantModulus-1%Secant,TD | | ASTMD882 | 28.0 | MPa |
抗张强度-MD(断裂) | | ASTMD882 | 17.0 | MPa |
抗张强度-TD(断裂) | | ASTMD882 | 14.0 | MPa |
伸长率-MD(断裂) | | ASTMD882 | 530 | % |
TensileElongation-TD(Break) | | ASTMD882 | 760 | % |
落锤冲击 | | ASTMD1709A | 410 | g |
埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 69 | g |
ElmendorfTearStrength-TD | | ASTMD1922 | 180 | g |
始封温度 | | | 67.0 | °C |
肖氏硬度(邵氏D) | | ASTMD2240 | 32 | |
脆化温度 | | ASTMD746 | <-73.0 | °C |
维卡软化温度 | | ASTMD1525 | 45.0 | °C |
熔融峰值温度 | | ASTMD3418 | 95.0 | °C |
光泽度(45°) | | ASTMD2457 | 43 | |
雾度 | | ASTMD1003 | 15 | % |