性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.929 | g/cm3 |
熔流率(熔体流动速率) | | ASTMD1238 | 0.55 | g/10min |
醋酸乙烯含量 | | | 7.5 | wt% |
薄膜厚度-经测试 | | | 32 | um |
SecantModulus-1%Secant,MD(32um,BlownFilm) | | ASTMD882 | 103 | MPa |
SecantModulus-1%Secant,TD(32um,BlownFilm) | | ASTMD882 | 110 | MPa |
TensileStrength-MD(Break,32um,BlownFilm) | | ASTMD882 | 24.1 | MPa |
TensileStrength-TD(Break,32um,BlownFilm) | | ASTMD882 | 25.5 | MPa |
TensileElongation-MD(Break,32um,BlownFilm) | | ASTMD882 | 380 | % |
TensileElongation-TD(Break,32um,BlownFilm) | | ASTMD882 | 550 | % |
落锤冲击(32um,吹塑薄膜) | | ASTMD1709 | 480 | g |
光泽度(45°,31.8um,吹塑薄膜) | | ASTMD2457 | 74 | |
雾度(31.8um,吹塑薄膜) | | ASTMD1003 | 4.8 | % |
补充信息 | | TestMethod | NominalValue | Unit |
BlownFilmMeltTemperature2 | | | 182to204 | °C |