性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.934 | g/cm3 |
熔流率(熔体流动速率) | | ASTMD1238 | 3.5 | g/10min |
醋酸乙烯含量 | | | 14.5 | wt% |
薄膜厚度-经测试 | | | 51 | um |
SecantModulus-1%Secant,MD2(51um,BlownFilm) | | ASTMD882 | 51.7 | MPa |
SecantModulus-1%Secant,TD2(51um,BlownFilm) | | ASTMD882 | 55.2 | MPa |
TensileStrength-MD2(Break,51um,BlownFilm) | | ASTMD882 | 22.1 | MPa |
TensileStrength-TD2(Break,51um,BlownFilm) | | ASTMD882 | 20.7 | MPa |
TensileElongation-MD2(Break,51um,BlownFilm) | | ASTMD882 | 700 | % |
TensileElongation-TD2(Break,51um,BlownFilm) | | ASTMD882 | 1000 | % |
DartDropImpact2(51um,BlownFilm) | | ASTMD1709 | 380 | g |
维卡软化温度 | | ASTMD1525 | 67.0 | °C |
熔融峰值温度 | | ASTMD3418 | 90.0 | °C |
Gloss3(45°,50.8um,BlownFilm) | | ASTMD2457 | 87 | |
Haze3(50.8um,BlownFilm) | | ASTMD1003 | 1.5 | % |
补充信息 | | TestMethod | NominalValue | Unit |
BlownFilmMeltTemperature | | | <193 | °C |
CastFilmMeltTemperature | | | <210 | °C |