性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.931 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 2.0 | g/10min |
醋酸乙烯含量 | | | 9.0 | wt% |
薄膜厚度-经测试 | | | 38 | um |
SecantModulus-1%Secant,MD(38um,BlownFilm) | | ASTMD882 | 96.5 | MPa |
SecantModulus-1%Secant,TD(38um,BlownFilm) | | ASTMD882 | 124 | MPa |
TensileStrength-MD(Break,38um,BlownFilm) | | ASTMD882 | 32.4 | MPa |
TensileStrength-TD(Break,38um,BlownFilm) | | ASTMD882 | 23.4 | MPa |
TensileElongation-MD(Break,38um,BlownFilm) | | ASTMD882 | 300 | % |
TensileElongation-TD(Break,38um,BlownFilm) | | ASTMD882 | 950 | % |
光泽度(45°,38.0um,吹塑薄膜) | | ASTMD2457 | 60 | |
Haze(38.1um,BlownFilm) | | ASTMD1003 | 4.8 | % |