性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.925 | g/cm3 |
熔流率(熔体流动速率) | | ASTMD1238 | 2.0 | g/10min |
醋酸乙烯含量 | | | 6.0 | wt% |
薄膜厚度-经测试 | | | 32 | um |
SecantModulus-1%Secant,MD2(32um,BlownFilm) | | ASTMD882 | 109 | MPa |
SecantModulus-1%Secant,TD2(32um,BlownFilm) | | ASTMD882 | 127 | MPa |
TensileStrength-MD2(Break,32um,BlownFilm) | | ASTMD882 | 30.0 | MPa |
TensileStrength-TD2(Break,32um,BlownFilm) | | ASTMD882 | 26.0 | MPa |
TensileElongation-MD2(Break,32um,BlownFilm) | | ASTMD882 | 440 | % |
TensileElongation-TD2(Break,32um,BlownFilm) | | ASTMD882 | 770 | % |
DartDropImpact2(32um,BlownFilm) | | ASTMD1709A | 180 | g |
Gloss3(45°,31.8um,BlownFilm) | | ASTMD2457 | 73 | |
Haze3(31.8um,BlownFilm) | | ASTMD1003 | 4.3 | % |