性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.931 | g/cm3 |
熔流率(熔体流动速率) | | ASTMD1238 | 0.55 | g/10min |
醋酸乙烯含量 | | | 4.0 | wt% |
摩擦系数(吹塑薄膜) | | ASTMD1894 | 0.50 | |
薄膜厚度-经测试 | | | 38 | um |
SecantModulus-1%Secant,MD2(38um,BlownFilm) | | ASTMD882 | 166 | MPa |
SecantModulus-1%Secant,TD2(38um,BlownFilm) | | ASTMD882 | 200 | MPa |
TensileStrength-MD2(Break,38um,BlownFilm) | | ASTMD882 | 22.0 | MPa |
TensileStrength-TD2(Break,38um,BlownFilm) | | ASTMD882 | 17.0 | MPa |
TensileElongation-MD2(Break,38um,BlownFilm) | | ASTMD882 | 230 | % |
TensileElongation-TD2(Break,38um,BlownFilm) | | ASTMD882 | 600 | % |
落锤冲击2(38um,吹塑薄膜) | | ASTMD1709 | 160 | g |
光泽度(45°,38.0um,吹塑薄膜) | | ASTMD2457 | 50 | |
Haze(38.1um,BlownFilm) | | ASTMD1003 | 13 | % |