性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTM D-792 | 1.77 | |
IZOD冲击强度 | 3.2mm | ASTM D-256 | 85 | J/m |
断裂伸长率 | 3.2mm | ASTM D-638 | 1.4 | % |
弯曲强度 | 3.2mm | ASTM D-790 | 177 | MPa |
拉伸强度 | 3.2mm | ASTM D-638 | 132 | MPa |
弯曲模量 | 3.2mm | ASTM D-790 | 15200 | MPa |
模压温度范围 | | | 30-95 | ℃ |
RTI,Mechanical with Impact | 3.0mm | UL 746-B | 220 | ℃ |
RTI,Mechanical with Impact | 3.0mm | UL 746-B | 240 | ℃ |
RTI,Mechanical with Impact | 1.0mm | UL 746-B | 240 | ℃ |
玻璃化转变温度 | | ASTM D-3418 | 120 | ℃ |
RTI,Electrical | 3.0mm | UL 746-B | 240 | ℃ |
RTI,Mechanical with Impact | 1.0mm | UL 746-B | 210 | ℃ |
干燥温度 | | | 135 | ℃ |
熔点 | | ASTM D-3418 | 335 | ℃ |
RTI,Electrical | 1.0mm | UL 746-B | 240 | ℃ |
热变形温度 | 1.80MPa | ASTM D-648 | 272 | ℃ |
解链温度范围 | | | 350-360 | ℃ |
124073667b7c7552467a7b71797c776161>[email protected] | | UL 746-B | V-0 | |
Thickness Tested | | UL 94 | 1.5 | mm |