| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 0.7 | % |
| 吸水率 | 饱和(23℃) | ASTM D-570 | 5.4 | % |
| 比重 | | ASTM D-792 | 1.38 | |
| 埃佐冲击强度 | ASTM D-256 | 23℃,DAM | 107 | j/m |
| 挠曲模量 | 23℃,50%RH | ASTM D-790 | 6205 | MPa |
| 挠曲模量 | 23℃,DAM | ASTM D-790 | 8963 | MPa |
| 挤剪强度 | 23℃,DAM | ASTM D-732 | 86 | MPa |
| 断裂伸长率 | 23℃,50%RH | ASTM D-638 | 4 | % |
| 泰伯磨耗量 | 50%RH | | 14 | cycles |
| 拉伸强度 | 23℃,50%RH | ASTM D-638 | 124.1 | MPa |
| 挠曲强度 | 23℃,DAM | ASTM D-790 | 262 | MPa |
| 洛氏硬度M | DAM | ASTM D-785 | M101 | |
| 断裂伸长率 | 23℃,DAM | ASTM D-638 | 3 | % |
| 拉伸强度 | 23℃,DAM | ASTM D-638 | 196.1 | MPa |
| 埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 133 | j/m |
| 损耗因数 | 24606569641514>[email protected] | ASTM D-150 | 0.02 | |
| 介电强度 | DAM | ASTM D-149 | 530 | volts/mil |
| 介电常数 | 2165606c611011>[email protected] | ASTM D-150 | 3.7 | |
| 介电强度 | 分步法(DAM) | ASTM D-149 | 440 | volts/mil |
| 体积电阻率 | DAM | ASTM D-257 | 10 | ohm-cm |
| 损耗因数 | eca8ada1acdddc>[email protected] | ASTM D-150 | 0.02 | |
| 体积电阻率 | 100%RH | ASTM D-257 | 10 | ohm-cm |
| 介电常数 | 80c4c1cdc0b1b0>[email protected] | ASTM D-150 | 4.5 | |
| 介电常数 | 100% da88929aebea>[email protected] | ASTM D-150 | 10.7 | |
| 介电常数 | 100% 590b11196869>[email protected] | ASTM D-150 | 25.0 | |
| 熔点 | 50%RH | ASTM D-789 | 255 | ℃ |
| 熔点 | DAM | ASTM D-789 | 255 | ℃ |
| 线性热膨胀系数 | | ASTM D-696 | 2.3×10 | m/m/℃ |
| 热畸变温度 | 1.8MPa | ASTM D-648 | 249 | ℃ |