性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
吸水率 | 饱和(23℃) | ASTM D-570 | 4.6 | % |
吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 0.5 | % |
比重 | | ASTM D-792 | 1.35 | |
洛氏硬度R | DAM | ASTM D-785 | R122 | |
挠曲模量 | 23℃,50%RH | ASTM D-790 | 5516 | MPa |
挠曲模量 | 23℃,DAM | ASTM D-790 | 6895 | MPa |
埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 128 | j/m |
断裂伸长率 | 23℃,50%RH | ASTM D-638 | 4 | % |
挤剪强度 | 23℃,DAM | ASTM D-732 | 72 | MPa |
洛氏硬度M | 50%RH | ASTM D-785 | M90 | |
洛氏硬度M | DAM | ASTM D-785 | M96 | |
断裂伸长率 | 23℃,DAM | ASTM D-638 | 3 | % |
洛氏硬度R | 50%RH | ASTM D-785 | R118 | |
泰伯磨耗量 | 50%RH | | 36 | cycles |
挠曲强度 | 23℃,DAM | ASTM D-790 | 228 | MPa |
埃佐冲击强度 | 23℃,DAM | ASTM D-256 | 128 | j/m |
拉伸强度 | 23℃,DAM | ASTM D-638 | 151.6 | MPa |
拉伸强度 | 23℃,50%RH | ASTM D-638 | 110.3 | MPa |
体积电阻率 | DAM | ASTM D-257 | 10 | ohm-cm |
介电强度 | (分步法)DAM | ASTM D-149 | 510 | volts/mil |
损耗因数 | f4b0b5b9b4c5c4>[email protected] | ASTM D-150 | 0.02 | |
介电强度 | 100%RH | ASTM D-149 | 255 | volts/mil |
介电常数 | 7c383d313c4d4c>[email protected] | ASTM D-150 | 4.2 | |
损耗因数 | d195909c91e0e1>[email protected] | ASTM D-150 | 0.02 | |
体积电阻率 | 100%RH | ASTM D-257 | 10 | ohm-cm |
介电强度 | DAM | ASTM D-149 | 630 | volts/mil |
介电常数 | 5612171b166766>[email protected] | ASTM D-150 | 3.4 | |
热畸变温度 | 1.8MPa | ASTM D-648 | 246 | ℃ |
线性热膨胀系数 | | ASTM D-696 | 1.8×10 | m/m/℃ |
熔点 | 50%RH | ASTM D-789 | 255 | ℃ |
熔点 | DAM | ASTM D-789 | 255 | ℃ |