| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 0.970 | g/cm3 |
| 密度 | | ISO1183 | 0.970 | g/cm3 |
| 熔流率（熔体流动速率）(190°C/2.16kg) | | ASTMD1238 | 4.5 | g/10min |
| 熔流率（熔体流动速率）(190°C/2.16kg) | | ISO1133 | 4.5 | g/10min |
| IonType | | | Zinc | |
| TensileStrength2(Yield,23°C,CompressionMolded) | | ASTMD638 | 15.9 | MPa |
| 抗张强度(断裂,23°C) | | ASTMD638 | 28.3 | MPa |
| 拉伸应力(断裂,23°C) | | ISO527-2 | 28.3 | MPa |
| 伸长率(断裂,23°C) | | ASTMD638 | 340 | % |
| 拉伸应变(断裂,23°C) | | ISO527-2 | 340 | % |
| 弯曲模量(23°C) | | ASTMD790 | 359 | MPa |
| 抗磨损性-NBSIndex | | ASTMD1630 | 368 | |
| 拉伸冲击强度 | | ASTMD1822 | 626 | kJ/m2 |
| 肖氏硬度(邵氏D) | | ASTMD2240 | 63 | |
| 肖氏硬度(邵氏D) | | ISO868 | 63 | |
| 维卡软化温度 | | ASTMD1525 | 57.0 | °C |
| 维卡软化温度 | | ISO306 | 57.0 | °C |
| 熔融峰值温度 | | ASTMD3418 | 82.0 | °C |
| 溶融温度（DSC） | | ISO3146 | 82.0 | °C |
| FreezingPoint | —— | ISO3146 | 42 | °C |
| FreezingPoint | —— | ASTMD3418 | 42 | °C |
| Haze(6350um) | | ASTMD1003 | 3.2 | % |