性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 3.2 | g/10min |
甲基丙烯酸含量 | | ExxonMobilMethod | 18.0 | wt% |
SecantModulus-1%Secant,MD | | ASTMD882 | 56.0 | MPa |
SecantModulus-1%Secant,TD | | ASTMD882 | 56.4 | MPa |
抗张强度-MD(断裂) | | ASTMD882 | 22.2 | MPa |
抗张强度-TD(断裂) | | ASTMD882 | 15.7 | MPa |
伸长率-MD(断裂) | | ASTMD882 | 350 | % |
TensileElongation-TD(Break) | | ASTMD882 | 790 | % |
落锤冲击 | | ASTMD1709A | 180 | g |
埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 93 | g |
ElmendorfTearStrength-TD | | ASTMD1922 | 350 | g |
维卡软化温度 | | ASTMD1525 | 57.0 | °C |