性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 5.2 | g/10min |
醋酸乙烯含量 | | ExxonMobilMethod | 14.9 | wt% |
SecantModulus-1%Secant,MD | | ASTMD882 | 77.1 | MPa |
SecantModulus-1%Secant,TD | | ASTMD882 | 81.4 | MPa |
抗张强度-MD(断裂) | | ASTMD882 | 29.6 | MPa |
抗张强度-TD(断裂) | | ASTMD882 | 19.4 | MPa |
伸长率-MD(断裂) | | ASTMD882 | 320 | % |
TensileElongation-TD(Break) | | ASTMD882 | 870 | % |
落锤冲击 | | ASTMD1709A | 96 | g |
埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 210 | g |
ElmendorfTearStrength-TD | | ASTMD1922 | 220 | g |
维卡软化温度 | | ASTMD1525 | 63.0 | °C |
光泽度(45°) | | ASTMD2457 | 86 | |
雾度 | | ASTMD1003 | 1.1 | % |