性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.932 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 0.19 | g/10min |
醋酸乙烯含量 | | ExxonMobilMethod | 10.1 | wt% |
SecantModulus-1%Secant,MD | | ASTMD882 | 107 | MPa |
SecantModulus-1%Secant,TD | | ASTMD882 | 121 | MPa |
抗张强度-MD(断裂) | | ASTMD882 | 35.3 | MPa |
抗张强度-TD(断裂) | | ASTMD882 | 35.1 | MPa |
伸长率-MD(断裂) | | ASTMD882 | 300 | % |
TensileElongation-TD(Break) | | ASTMD882 | 620 | % |
落锤冲击 | | ASTMD1709A | 660 | g |
埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 91 | g |
ElmendorfTearStrength-TD | | ASTMD1922 | 85 | g |
维卡软化温度 | | ASTMD1525 | 83.0 | °C |
光泽度(45°) | | ASTMD2457 | 70 | |
雾度 | | ASTMD1003 | 5.0 | % |