性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
熔流率(熔体流动速率) | 190°C/2.16kg | ASTMD1238 | 0.45 | g/10min |
熔流率(熔体流动速率) | 190°C/21.6kg | ASTMD1238 | 30 | g/10min |
SecantModulus-1%Secant,MD | | ASTMD882 | 1080 | MPa |
SecantModulus-1%Secant,TD | | ASTMD882 | 1610 | MPa |
抗张强度-MD(屈服) | | ASTMD882 | 34.5 | MPa |
TensileStrength-TD(Yield) | | ASTMD882 | 13.1 | MPa |
抗张强度-MD(断裂) | | ASTMD882 | 83.8 | MPa |
抗张强度-TD(断裂) | | ASTMD882 | 36.6 | MPa |
伸长率-MD(断裂) | | ASTMD882 | 420 | % |
TensileElongation-TD(Break) | | ASTMD882 | 4.0 | % |
落锤冲击 | | ASTMD1709A | <40 | g |
埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 8.5 | g |
ElmendorfTearStrength-TD | | ASTMD1922 | 780 | g |