性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
熔流率(熔体流动速率) | —— | ASTMD1238 | 46 | g/10min |
熔流率(熔体流动速率) | 190°C/2.16kg | ASTMD1238 | 0.70 | g/10min |
SecantModulus-1%Secant,MD | | ASTMD882 | 1200 | MPa |
SecantModulus-1%Secant,TD | | ASTMD882 | 1700 | MPa |
抗张强度-MD(断裂) | | ASTMD882 | 60.0 | MPa |
TensileStrength-TD2(Break) | | ASTMD882 | 31.0 | MPa |
TensileElongation-MD2(Break) | | ASTMD882 | 510 | % |
TensileElongation-TD2(Break) | | ASTMD882 | 2.0 | % |
落锤冲击 | | ASTMD1709A | <30 | g |
埃尔曼多夫抗撕强度-MD | | ASTMD1922 | 10 | g |
ElmendorfTearStrength-TD | | ASTMD1922 | 200 | g |
维卡软化温度 | | ASTMD1525 | 127 | °C |