性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.13 | g/cm3 |
密度 | | ISO1183 | 1.12 | g/cm3 |
熔流率(熔体流动速率)(190°C/21.6kg) | | ASTMD1238 | 16 | g/10min |
熔流率(熔体流动速率)(190°C/21.6kg) | | ISO1133 | 16 | g/10min |
抗张强度2(屈服) | | ASTMD638 | 32.0 | MPa |
拉伸应力(断裂) | | ISO527-2/50 | 32.0 | MPa |
伸长率2(屈服) | | ASTMD638 | 14 | % |
伸长率2(断裂) | | ASTMD638 | 40 | % |
拉伸应变(断裂) | | ISO527-2/50 | 14 | % |
弯曲模量3 | | ASTMD790 | 1950 | MPa |
弯曲模量4 | | ISO178 | 1800 | MPa |
悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 580 | J/m |
悬壁梁缺口冲击强度 | -20°C | ISO180 | 26 | kJ/m2 |
悬壁梁缺口冲击强度 | 23°C | ISO180 | 42 | kJ/m2 |
Multi-AxialInstrumentedImpactEnergy(0°C) | | ASTMD3763 | 14.5 | J |
载荷下热变形温度(0.45MPa,未退火) | | ASTMD648 | 98.0 | °C |
热变形温度(0.45MPa,未退火) | | ISO75-2/B | 85.0 | °C |
载荷下热变形温度(1.8MPa,未退火) | | ASTMD648 | 55.0 | °C |