性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.23 | g/cm3 |
MeltMass-FlowRate(MFR)(250°C/11.6kg) | | ASTMD1238 | 3.0to10 | g/10min |
收缩率-流动 | | ASTMD955 | 0.50to0.70 | % |
抗张强度(屈服,3.17mm) | | ASTMD638 | 72.4 | MPa |
TensileStrength(Break,3.18mm) | | ASTMD638 | 58.6 | MPa |
伸长率(屈服,3.18mm) | | ASTMD638 | 3.5 | % |
伸长率(断裂,3.18mm) | | ASTMD638 | 8.0 | % |
弯曲模量(3.17mm) | | ASTMD790 | 3450 | MPa |
FlexuralStrength(Break,3.18mm) | | ASTMD790 | 110 | MPa |
简支梁缺口冲击强度(23°C) | | ISO179/2C | 8.4 | kJ/m2 |
悬壁梁缺口冲击强度(23°C,3.18mm) | | ASTMD256 | 110 | J/m |
悬壁梁缺口冲击强度(23°C) | | ISO180/1A | 8.4 | kJ/m2 |
载荷下热变形温度(0.45MPa,未退火,3.18mm) | | ASTMD648 | 110 | °C |
载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 104 | °C |
维卡软化温度 | | ASTMD15252 | 127 | °C |
RTIElec | 1.5mm | UL746 | 65.0 | °C |
RTIElec | 3.0mm | UL746 | 65.0 | °C |
RTIImp | 1.5mm | UL746 | 65.0 | °C |
RTIImp | 3.0mm | UL746 | 65.0 | °C |
RTIStr | 1.5mm | UL746 | 65.0 | °C |
RTIStr | 3.0mm | UL746 | 65.0 | °C |
体积电阻率 | | ASTMD257 | 1.0E+16 | ohmscm |
UL阻燃等级 | 1.5mm | UL94 | V-0 | |
UL阻燃等级 | 3.0mm | UL94 | V-0 | |