性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.28 | g/cm3 |
MeltMass-FlowRate(MFR)(250°C/11.6kg) | | ASTMD1238 | 1.0to8.0 | g/10min |
收缩率-流动(3.18mm) | | ASTMD955 | 0.10to0.40 | % |
抗张强度(屈服,3.17mm) | | ASTMD638 | 110 | MPa |
TensileStrength(Break,3.18mm) | | ASTMD638 | 110 | MPa |
伸长率(断裂,3.18mm) | | ASTMD638 | 2.0 | % |
弯曲模量(3.17mm) | | ASTMD790 | 7580 | MPa |
弯曲强度(3.18mm) | | ASTMD790 | 159 | MPa |
简支梁缺口冲击强度(23°C) | | ISO179/1 | 6.3 | kJ/m2 |
悬壁梁缺口冲击强度 | -30°C,3.18mm | ASTMD256 | 53 | J/m |
悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 80 | J/m |
悬壁梁缺口冲击强度(23°C) | | ISO180/1A | 6.3 | kJ/m2 |
洛氏硬度(L计秤) | | ASTMD785 | 108 | |
载荷下热变形温度(0.45MPa,未退火,3.18mm) | | ASTMD648 | 149 | °C |
载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 143 | °C |
维卡软化温度 | | ASTMD15252 | 152 | °C |
RTIElec | 1.5mm | UL746 | 65.0 | °C |
RTIElec | 3.0mm | UL746 | 65.0 | °C |
RTIImp | 1.5mm | UL746 | 65.0 | °C |
RTIImp | 3.0mm | UL746 | 65.0 | °C |
RTIStr | 1.5mm | UL746 | 65.0 | °C |
RTIStr | 3.0mm | UL746 | 65.0 | °C |
体积电阻率 | | ASTMD257 | 1.0E+16 | ohmscm |
UL阻燃等级 | 1.5mm,ALL | UL94 | HB | |
UL阻燃等级 | 3.0mm,ALL | UL94 | HB | |