性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.956 | g/cm3 |
熔流率(熔体流动速率)(190°C/21.6kg) | | ASTMD1238 | 9.0 | g/10min |
抗环境应力开裂2 | 50°C,1.91mm,10%IgepalCO-630 | ASTMD1693B | 500 | hr |
抗环境应力开裂2 | 50°C,3.18mm,100%IgepalCO-630 | ASTMD1693A | >1000 | hr |
肖氏硬度(邵氏D) | | ASTMD2240 | 62 | |
抗张强度(屈服) | | ASTMD638 | 32.0 | MPa |
伸长率(断裂) | | ASTMD638 | 800 | % |
弯曲模量-正切 | | ASTMD790 | 1.32 | MPa |
拉伸冲击强度 | | ASTMD1822 | 450 | kJ/m2 |
脆化温度 | | ASTMD746 | <-60.0 | °C |
维卡软化温度 | | ASTMD1525 | 124 | °C |
熔融温度 | | DSC | 131 | °C |
HeatDeflectionTemperature | | ASTMD648 | 74 | °C |