性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度(基体树脂) | | ISO1183 | 0.924 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ISO1133 | 3.0 | g/10min |
含水量 | | KarlFisher | <200 | ppm |
拉伸应力2(屈服) | | ISO527-2/250 | >17.0 | MPa |
拉伸应变2(断裂) | | ISO527-2/250 | >450 | % |
ChangeinTensileProperties-AfterAgeing168h2(135°C) | | IEC60811-401 | <20 | % |
热固性 | Elongationunderload,0.20MPa:200°C | IEC60811-507 | 75 | % |
热固性 | Permanentdeformation,0.20MPa:200°C | IEC60811-507 | 5.0 | % |
体积电阻率 | | IEC60093 | >1.0E+15 | ohmscm |
介电强度 | | IEC60243-1 | >22 | kV/mm |
介电常数(50Hz) | | IEC60250 | 2.30 | |
耗散因数(50Hz) | | IEC60250 | 5.0E-4 | |
MethanolWash | | 内部方法 | <500 | ppm |
MonsantoODR | | ASTMD2084 | 37.0到47.0 | dNm |