| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度3 | | ISO1183 | 0.940 | g/cm3 |
| 熔流率（熔体流动速率）(190°C/2.16kg) | | ISO1133 | 1.0 | g/10min |
| EnvironmentalStress-CrackingResistance(50°C,10%Igepal,F20) | | IEC60811-4-1/B | >96.0 | hr |
| 拉伸应力(屈服) | | ISO527-2/250 | >20.0 | MPa |
| 拉伸应变(断裂) | | ISO527-2/250 | >300 | % |
| 肖氏硬度(邵氏D,1秒) | | ISO868 | 55 | |
| 脆化温度 | | ASTMD746 | <-76.0 | °C |
| 热固性 | 200°C3 | IEC60811-2-1 | 60 | % |
| 热固性 | 200°C4 | IEC60811-2-1 | 0.0 | % |
| ChangeinTensileStress(135°C,240hr) | | IEC60811-1-2 | <25 | % |
| 体积电阻率 | | IEC60093 | >1.0E+16 | ohmscm |
| 介电强度 | | IEC60243-1 | >20 | kV/mm |
| 介电常数(50Hz) | | IEC60250 | <2.50 | |
| 耗散因数(50Hz) | | IEC60250 | <6.0E-4 | |
| 补充信息 | | TestMethod | NominalValue | Unit |
| Crosslinking | 23°C,700.0um5 | | 1.5 | day |
| Crosslinking | 23°C,1.80mm5 | | 7.0 | day |
| Crosslinking | 90°C,700.0um6 | | <15.0 | min |
| Crosslinking | 90°C,1.80mm6 | | 1.00 | hr |