性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重(基体树脂) | | ASTMD792 | 0.923 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 2.2 | g/10min |
抗张强度2 | | ASTMD638 | 17.0 | MPa |
伸长率2(断裂) | | ASTMD638 | 400 | % |
空气中拉伸强度的变化率(136°C,168hr) | | ASTMD638 | 10 | % |
脆化温度 | | ASTMD746 | <-76.0 | °C |
HotCreep3 | Elongationunderload:150°C | ICEAT-28-562 | <75 | % |
HotCreep3 | Permanentdeformation:150°C | ICEAT-28-562 | <5.0 | % |
热固性 | Elongationunderload:200°C4 | IEC60811-507 | <75 | % |
热固性 | Permanentdeformation:200°C5 | IEC60811-507 | <5.0 | % |
体积电阻率 | | ASTMD257 | >1.0E+16 | ohmscm |
介电强度 | | ASTMD149 | >21 | kV/mm |
介电常数(50Hz) | | ASTMD150 | <2.30 | |
耗散因数(50Hz) | | ASTMD150 | 5.0E-4 | |