性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
Density(BaseResin) | | ISO1183 | 0.922 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ISO1133 | 2.0 | g/10min |
Moisture | | KarlFisher | <200 | ppm |
拉伸应力 | | ISO527-2/500 | >17.0 | MPa |
拉伸应变(断裂) | | ISO527-2/500 | >450 | % |
热固性2 | Elongationunderload:200°C | IEC60811-507 | <180 | % |
热固性2 | Permanentdeformation:200°C | IEC60811-507 | <15 | % |
ChangeinTensileStrainatBreakinAir(135°C,168hr) | | IEC60811-401 | <20 | % |
体积电阻率 | | IEC60093 | >1.0E+16 | ohmscm |
介电强度3 | | IEC60243-1 | >22 | kV/mm |
介电常数(50Hz) | | IEC60250 | <2.30 | |
耗散因数(50Hz) | | IEC60250 | <3.0E-4 | |
补充信息 | | TestMethod | NominalValue | Unit |
GottfertElastograph | | ISO6502 | <0.65 | Nm |
MethanolWash | | InternalMethod | <800 | ppm |