性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度3 | | ISO1183 | 0.923 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ISO1133 | 1.0 | g/10min |
EnvironmentalStress-CrackingResistance(50°C,10%Igepal,F20) | | IEC60811-4-1/B | >96.0 | hr |
拉伸应力 | | ISO527-2/250 | >15.0 | MPa |
拉伸应变(断裂) | | ISO527-2/250 | >300 | % |
肖氏硬度(邵氏D,1秒) | | ISO868 | 52 | |
脆化温度 | | ASTMD746 | <-76.0 | °C |
热固性3 | Elongationunderload:200°C | IEC60811-2-1 | 60 | % |
热固性3 | Permanentdeformation:200°C | IEC60811-2-1 | 0.0 | % |
MechanicalPropertiesAfterAginginAirOven,135°C,240hr(ChangeinTensileStrength) | | IEC60811 | <-75 | % |
体积电阻率 | | IEC60093 | >1.0E+16 | ohmscm |
介电强度 | | IEC60243-1 | >22 | kV/mm |
介电常数(50Hz) | | IEC60250 | <2.30 | |
耗散因数(50Hz) | | IEC60250 | <5.0E-4 | |