| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度3 | | ISO1183 | 1.15 | g/cm3 |
| 熔流率（熔体流动速率）3(190°C/2.16kg) | | ISO1133 | 0.90 | g/10min |
| WaterAbsorption4(70°C) | | IEC60811-1-3 | 0.100 | mg/cm2 |
| TensileStress5(Yield) | | ISO527-2/50 | 13.0 | MPa |
| TensileStrain5(Break) | | ISO527-2 | 550 | % |
| 弯曲模量3 | | ISO178 | 215 | MPa |
| ShoreHardness3(ShoreD,15sec) | | ISO868 | 40 | |
| 脆化温度3 | | ISO974 | <-60.0 | °C |
| ColdBend5(-40°C) | | IEC60811-1-4 | Pass | |
| ColdImpact5(-40°C) | | IEC60811-1-4 | Pass | |
| TemperatureIndex-Compound | | ISO4589-3 | 200 | °C |
| 拉伸强度的变化率 | ——6 | IEC60811-1-2 | >-80 | % |
| 拉伸强度的变化率 | 100°C,240hr | IEC60811-1-2 | >-80 | % |
| 体积电阻率3 | | IEC60093 | 1.0E+16 | ohmscm |
| 介电强度 | | IEC60243-1 | 20 | kV/mm |
| 极限氧指数3 | | | 27 | % |
| NBSSmokeDensity | ——7 | | 6.0 | min |
| NBSSmokeDensity | ——8 | | 49.0 | |
| NBSSmokeDensity | ——9 | | 20.0 | min |
| NBSSmokeDensity | ——10 | | 104 | |
| 补充信息 | | TestMethod | NominalValue | Unit |
| BreakdownDuration5 | | IEC60227-2/2.3 | Pass | |
| BreakdownVoltage5 | | ISO6722 | 36000 | V |
| ConeCalorimeter | AverageHeatRelease11 | ISO5660 | 244 | kW/m2 |
| ConeCalorimeter | CO11 | ISO5660 | 0.230 | kg/m3 |
| ConeCalorimeter | CO211 | ISO5660 | 17.0 | kg/m3 |
| ConeCalorimeter | HeatCubustion12 | ISO5660 | 29.0 | |
| ConeCalorimeter | Ignitiontime11 | ISO5660 | 2.1 | min |
| ConeCalorimeter | MaxHeatRelease11 | ISO5660 | 400 | kW/m2 |
| ConeCalorimeter | SmokeObscuration13 | ISO5660 | 520 | |
| Corrosion-ofCombustionFumes14 | | IEC60754-2 | 1.50 | uS/cm |
| PressureTest15(90°C) | | IEC60811-3-1 | <50 | % |